1: DIN S355JR Steel Introduction
S355JR is a low alloy high strength structural steel conforming to European standard EN 10025. S355JR steel in China is low alloy high strength structural steel with hardness of 70-80B and yield strength of 300-400MPa. And has very good processing formability and welding performance, as well as excellent low temperature toughness.
2: DIN S355K2 Steel Equivalent
| Country | China | Japan | Germany | USA | British |
| Standard | GB/T 1591 | JIS | DIN (W-Nr.) EN 10025-2 / DIN17100 |
AISI/ASTM | BS |
| Grade | Q355E | / | S355K2 | / | / |
3: DIN S355JR Steel Chemical Composition
| Grade | C | Si | Mn | P | S | Cr | Cu | Ni |
| S355JR | 0.22 | 0.55 | 1.60 | 0.025 | 0.025 | / | 0.55 | / |
| Q355B | 0.24 | 0.55 | 1.60 | 0.035 | 0.035 | 0.30 | 0.40 | 0.30 |
4: DIN S355JR Steel Mechanical Properties
The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, kindly contact the salesman.
5: DIN S355JR Steel Overviews
| Size | Round | Dia 6-1200mm |
| Plate/Flat/Block | Thickness 6mm-500mm |
|
| Width 20mm-1000mm |
||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | |
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | |
| Delivery condition | Forged; Hot rolled; Cold drawn | |
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
| Payment terms | T/T;L/C;/Money gram/ Paypal | |
| Trade terms | FOB; CIF; C&F; etc.. | |
| Delivery time | 30-45 days | |
| Application | S355JR is used for medium strength structural parts of aircraft, propeller blades, transportation vehicles and building structural parts, and medium strength bolts and rivets of aircraft. It is also applied to aircraft skin, frame, rib, spar, rivet, etc. | |
6: Delivery Condition
For hot forged bar, usually the delivery condition is hot forged, annealed/solid solution, rough turned/Black surface.
For hot rolled bar, usually the delivery condition is hot rolled, annealed/solid solution, Black surface.
For hot rolled plate, usually the delivery condition is hot rolled, annealed/solid solution, black surface.
For cold drawn bar, usually the delivery condition is cold drawn, annealed/QT, peeled/black surface
| GB GB/T 1299 |
JIS JIS G4404 |
DIN (W-Nr.) DIN EN ISO4957 |
AISI/ASTM ASTM A681 |
BS BS 4659 |
| Cold Work Tool Steel | ||||
| Cr12 | SKD1 | 1.2080/X210Cr12 | D3 | |
| Cr5Mo1V | SKD12 | 1.2363/X100CrMoV5 | A2/T30102 | BA2 |
| Cr12MoV | 1.2601 | D5 | ||
| Cr12Mo1V1 | SKD11 | 1.2379/X153CrMo12 | D2 | |
| X210CrW12 | SKD2 | 1.2436 | D6 | |
| 9CrWMn | SKS3 | 1.2510/100MnCrW4 | O1 | |
| 9Mn2V | 1.2842 / 90MnCrV8 | O2 | B02 | |
| 5CrNiMo | SKT4 | 1.2713 | L6/T61206 | BH224/5 |
| Hot work Tool Steel | ||||
| 1.2355/50CrMoV13-15 | S7/T41907 | |||
| 5CrNiMoV | 1.2714 | 6F3 | ||
| 5CrNi4Mo | 1.2767 | 6F7 | ||
| SKD7 | 1.2365/32CrMoV12-28 | H10/T20810 | BH10 | |
| 4Cr5MoV | SKD6 | 1.2343/X37CrMoV5-1 | H11/T20811 | BH11 |
| 4Cr5MoSiV1 | SKD61 | 1.2344/X40CrMoV5-1 | H13 | |
| SKD62 | 1.2605/X35CrWMoV5 | H12/T20812 | BH12 | |
| 3Cr2W8V | SKD5 | 1.2581 | H21 | |
| Plastic Mould Steel | ||||
| 3Cr2Mo | 1.2311 | P20 | ||
| NAK80 | 1.2312 | P20+S / P21 | ||
| 3Cr2MnNiMo | 1.2738 | P20+Ni / 718 | ||
| 4Cr13 | SUS420J2 | 1.2083 | 415 | |
| 3Cr17+S | SUS420F | 1.2085 | ||
| 3Cr17Mo | SUS420J | 1.2316 | ||
| Engineering Steel | ||||
| GB GB/T 699 |
JIS JIS G4051 |
DIN (W-Nr.) EN 10083-2 |
AISI/ASTM ASTM A20 |
EN / BS |
| 1018 | EN2C | |||
| 20 | S20C | C20/1.1151 | 1020 | EN3B /070M20 |
| S35C | C35 | 1035 | ||
| 1040 | EN8/080M40 | |||
| 45 | S45C | C45/1.1191 | 1045 | EN8D/C45E |
| 50 | S50C | 1050 | ||
| S55C | 1055 | EN9/070M55 | ||
| Q345 | S355/ST52-3/1.1170 | EN14/150M19 | ||
| GB GB/T 3077 |
JIS JIS G4105/JIS G4103 |
DIN (W-Nr.) EN 10250 |
AISI/ASTM ASTM A29 |
BS BS 970 |
| 40Cr | SCr440 | 41Cr4(1.7035) | 5140 | |
| SCM420 | 18CrMo4/1.7243 | 4118 | ||
| 30CrMo | SCM430 | 25CrMo4/1.7218 | 4130 | 708A25/708M25 |
| 42CrMo | SCM440 | 42crmo4/1.7225 | 4140 | EN19/709M40 |
| 4145 | ||||
| 4330 | ||||
| 40CrNiMoA | SNCM 439/SNCM8 | 36CrNiMo4/1.6511 | 4340 | EN24/817M40 |
| 40NiMoCr10-5/1.6745 | EN26 | |||
| 34CrNiMo6 / 1.6582 | 4337 | |||
| 30CrNiMo16-6/1.6747 | EN30B/835M30 | |||
| 32CrMo12/1.7361 | EN40B/722M24 | |||
| SCM415 | 16MnCr5 / 1.7131 | 5115 | ||
| 15CrNi6/1.5919 | 3115 | |||
| 16NiCr4/1.5714 | EN351/635M15 | |||
| 4615/4617 | EN34/665M17 | |||
| 14NiCr4/1.5752 | 3310/3415 | EN36/655M13 | ||
| 15NiCrMo16-5/1.6723 | EN39/835M15 | |||
| 18CrNiMo7-6 (1.6587) | 4815 | |||
| SNCM220 | 1.6523/21NiCrMo2 | 8620 | 805M20 | |
| 20CrNiMo5 | EN353 | |||
| GCr15 | 52100/1.3505 | EN31/535A99 | ||
| Stainless Steel | ||||
| SUS440C | X105CrMo17/1.4125 | S44004/440C | ||
| Wear-resisting Steel | ||||
| GB | JIS | DIN (W-Nr.) | AISI/ASTM | SSAB |
| NM400 | HB400 | |||
| NM500 | HB500 | |||
| Spring Steel | ||||
| GB | JIS | DIN (W-Nr.) | AISI/ASTM | SSAB |
| 65MN | 1066 | |||
| 60Si2Mn | SUP6 | 60Si7 | 9260 | |
| 60Si2MnA | SUP7 | 60Si7 | 9260 | |
| 55CrMnA | SUP9 | 55Cr3 | 5155 | |
| 60CrMnA | SUP9A | 5160 | ||
| 50CrVA | SUP10 | 51CrV4 | 6150 | |
| High Speed Steel | ||||
| GB | JIS JIS G4403 |
DIN (W-Nr.) DIN EN ISO 4957 |
AISI/ASTM ASTM A600 |
BS BS 4659 |
| SKH51 | 1.3343 | M2 | ||
| SKH55 | 1.3243/HS6-5-2-5 | M35 | ||
| SKH59 | 1.3247/HS2-9-1-8 | M42 | ||
| SKH2 | HS18-0-1/1.3355 | T1 | ||
| SKH3 | S 18-1-2-5/1.3255 | T4/T12004 | ||
| SKH4 | 1.3265/S18-1-2-10 | T5/T12005 | BT5 | |
| All kinds of forging parts according to Drawing | ||||
Hunan Qilu Industrial Co., Ltd has the capacity to forge round steel, steel flat, square steel, module, shaft and roller, etc. The main specifications of the products include Φ80-1000mm forging materials and 80-1200mm square billets and which the maximum piece weight can reach 50T.
The company owns advanced special steel smelting facilities and forging processing equipments, the main steel-making equipment include 2 sets of 50t ultra-high power electric arc furnaces,2 sets of 60t LF refining furnaces,1 set of 60t vacuum degassing refining furnace and 4 sets of 1-20t electroslag re-melting furnaces.
Q1:Are you trading company or manufacturer ?
Fornecedores com licênças comerciais verificadas
Fornecedor Auditado 